References of manufacturer for all underlays and top layers:
The rolls should be stored and transported vertically and protected against moisture and heat by temperature more than 40°C
In the cold season, the rolls should be brought at the temperature more then +5°C not less 12 hours before use.
BIKROELAST PV S4b
|
Characteristics |
Standard |
Measurement unit |
BIKROELAST
PV S4b |
|
Thickness |
LST EN 1849-1 |
mm |
3±0,2 |
|
Base |
|
- |
Polyester 160 g/m² |
|
Surfacing |
|
- |
slate |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
4±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
>600/ >400 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+85 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-10 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
>100 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
|
External fire performance |
LST EN 13501-5 |
- |
- |
BIKROELAST V S3s
|
Characteristics |
Standard |
Measurement unit |
BIKROELAST
V S3s |
|
Thickness |
LST EN 1849-1 |
mm |
3±0,2 |
|
Base |
|
- |
Fibre glass 70 g/m² |
|
Surfacing |
|
- |
Film or sand |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
4±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
>400/ >200 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+85 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-10 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
>100 |
|
Roll dimensions |
LST EN 1848-1 |
m |
15x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
|
External fire performance |
LST EN 13501-5 |
- |
|
BIPOL PV S3,5b
|
Characteristics |
Standard |
Measurement unit |
BIPOL
PV S3,5b |
|
Thickness |
LST EN 1849-1 |
mm |
3,5±0,2 |
|
Base |
|
- |
polyester 160 g/m² |
|
Surfacing |
|
- |
slate |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
4,25 ±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
>600/ >300 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
>30/ >30 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+80 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-15 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
>100 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
TECHNOELAST PV S4b
|
Characteristics |
Standard |
Measurement unit |
TECHNOELAST PV S4b |
|
Thickness |
LST EN 1849-1 |
mm |
4,2±0,2 |
|
Base |
|
- |
polyester 200 g/m² |
|
Surfacing |
|
- |
slate |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
5,1±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
≥850/ ≥600 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
≥40/ ≥40 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+100 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-25 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
≥300 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
|
External fire performance |
LST EN 13501-5 |
- |
Broof (t1) |
TECHNOELAST PV S4s
|
Characteristics |
Standard |
Measurement unit |
TECHNOELAST PV S4s |
|
Thickness |
LST EN 1849-1 |
mm |
4±0,2 |
|
Base |
|
- |
polyester 200 g/m² |
|
Surfacing |
|
- |
sand |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
5,0±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
≥850/ ≥600 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
≥40/ ≥40 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+100 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-25 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
≥300 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
|
External fire performance |
LST EN 13501-5 |
- |
- |
BALT PV S4b
|
Characteristics |
Standard |
Measurement unit |
BALT PV S4b |
|
Thickness |
LST EN 1849-1 |
mm |
4,2±0,2 |
|
Base |
|
- |
polyester 200 g/m² |
|
Surfacing |
|
- |
slate |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
4,9±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
>800/ >600 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
>40/ >40 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+95 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-20 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
>200 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
|
External fire performance |
LST EN 13501-5 |
- |
Broof (t1) |
BALT PV S3s
|
Characteristics |
Standard |
Measurement unit |
BALT PV S3s |
|
Thickness |
LST EN 1849-1 |
mm |
3,0±0,2 |
|
Base |
|
- |
polyester 160 g/m² |
|
Surfacing |
|
- |
sand |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
4,0±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
>700/ >500 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
>40/ >40 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+95 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-20 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
>100 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
|
External fire performance |
LST EN 13501-5 |
- |
- |
UNIFLEKS PV S4b
|
Characteristics |
Standard |
Measurement unit |
UNIFLEKS PV S4b |
|
Thickness |
LST EN 1849-1 |
mm |
4,2±0,2 |
|
Base |
|
- |
polyester 180 g/m² |
|
Surfacing |
|
- |
slate |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
4,9±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
≥800/ ≥450 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
≥40/ ≥40 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+95 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-15 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
≥200 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
UNIFLEKS PV S3s
|
Characteristics |
Standard |
Measurement unit |
UNIFLEKS PV S3s |
|
Thickness |
LST EN 1849-1 |
mm |
3,2±0,2 |
|
Base |
|
- |
polyester 160 g/m² |
|
Surfacing |
|
- |
sand |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
4,0±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
≥800/ ≥450 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
≥40/ ≥40 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+95 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-15 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
≥100 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
UNIFLEKS V S4b
|
Characteristics |
Standard |
Measurement unit |
UNIFLEKSV S4b |
|
Thickness |
LST EN 1849-1 |
mm |
4,0±0,2 |
|
Base |
|
- |
fibre glass 70 g/m² |
|
Surfacing |
|
- |
slate |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
5,1±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
≥400/ ≥300 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
≥5/ ≥5 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+95 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-15 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
≥100 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
UNIFLEKS V S3s
|
Characteristics |
Standard |
Measurement unit |
UNIFLEKS V S3s |
|
Thickness |
LST EN 1849-1 |
mm |
3,2±0,2 |
|
Base |
|
- |
fibre glass 70 g/m² |
|
Surfacing |
|
- |
sand |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
4,0±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
≥400/ ≥300 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
≥2/ ≥2 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+95 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
-15 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
≥100 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
|
Flammability |
LST EN 13501-1:2002 |
type |
E |
BIT V13b
|
Characteristics |
Standard |
Measurement unit |
BIT V13b |
|
Thickness |
LST EN 1849-1 |
mm |
2,8±0,2 |
|
Base |
|
- |
Fibre glass 70 g/m² |
|
Surfacing |
|
- |
slate |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
3,8±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
>400/ >300 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
>2/ >2 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+80 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
0 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
>100 |
|
Roll dimensions |
LST EN 1848-1 |
m |
10x1 |
BIT V13s
|
Characteristics |
Standard |
Measurement unit |
BIT V13s |
|
Thickness |
LST EN 1849-1 |
mm |
2,0±0,2 |
|
Base |
|
- |
Fibre glass 70 g/m² |
|
Surfacing |
|
- |
sand |
|
Weight /1 m² |
LST EN 1849-1 |
kg |
2,6±0,25 |
|
Tensile strength: lengthwise/transverse |
LST EN 12311-1 |
N/50mm |
>400/ >300 |
|
Relative elongation: lengthwise/transverse |
LST EN 12311-1 |
% |
>2/ >2 |
|
Heat resistance, not less than |
LST EN 1110 |
° C |
+80 |
|
Flexibility, not higher than |
LST EN 1109 |
° C |
0 |
|
Water imperviousness after 24 hours |
LST EN 1928:2000 B method |
kPa |
>80 |
|
Roll dimensions |
LST EN 1848-1 |
m |
15x1 |
UNIFLEKS EMM
|
Characteristics |
Test method / (classification) |
Units |
Expression of resulta |
Value or statement |
Declarated tolerances |
|
Visible defects |
EN 1850-1 |
– |
Visible defects |
- |
|
|
Length |
EN 1848-1 |
m |
MLV |
15,0 |
- 0% |
|
Width |
EN 1848-1 |
m |
MLV |
1,0 |
- 0% |
|
Straightness |
EN 1848-1 |
– |
Pass |
10m ≤ 20mm |
|
|
Mass per unit area |
EN 1849-1 |
kg/m2 |
MDV |
1,6 |
±0,2 kg/ m2 |
|
Thickness |
EN 1849-1 |
mm |
MDV |
1,5 |
±0,1mm |
|
Watertightness |
EN 1928:2000, Method B |
– |
Pass |
10 kP |
- 0 kPa |
|
Watertightness after stretching at low temperature |
EN 13897 |
% |
MLV |
- |
|
|
External fire performance |
ENV 1187 |
– |
EN 13501-5 |
NPD |
|
|
Reaction to fire |
EN 13501-1 |
– |
EN 13501-1 (see NOTE in 5.2.5.2) |
F |
|
|
Peel resistance of joint |
EN 12316-1 |
N/50 mm |
MDV |
- |
|
|
Joint strength (Shear resistance) |
EN 12317-1 |
N/50 mm |
MDV |
- |
|
|
Tensile properties : maximum tensile force |
EN 12311-1 |
N/50 mm |
MDV |
400 / 250 |
-10% |
|
Tensile properties: elongation |
12311-1 |
% |
MDV |
40 / 40 |
-10% |
|
Resistance to impact |
EN 12691 |
mm |
MLV |
- |
|
|
Resistance to static loading |
EN 12730 |
Kg |
MLV |
- |
|
|
Resistance to tearing (nail shank) |
EN 12310-1 |
N |
MDV |
100 |
-10% |
|
Resistance to root penetration |
prEN 13948 |
– |
Pass |
– |
|
|
Dimensional stability |
EN 1107-1 |
% |
MLV |
- |
|
|
Form stability under cyclic temperature change |
EN 1108 |
mm |
MLV |
- |
|
|
Flexibility at low temperature |
EN 1109 |
°C |
MLV |
-15 |
|
|
Flow resistance at elevated temperature |
EN 1110 |
°C |
MLV |
100 |
|
|
Artificial ageing by long term exposure to elevated temperature |
EN 1296 |
See EN 1109 |
MDV |
- |
|
|
Artificial ageing by long term exposure to combination of UV radiation, elevated temperature and water |
EN 1297 |
See
EN 1850-1 |
Pass |
– |
|
|
Adhesion of granules |
EN 12039 |
% |
MDV |
- |
|
|
Water vapour transmission properties |
EN 1931 |
– |
μ = MDV or 20 000 |
NPD |
|
|
a - MLV: manufacturer limiting value according to 3.9 EN 13707; MDV: manufacturer declarated value according to 3.10 EN 13707 3.
– not relevant
NPD- no performance determined |
UNIFLEKS EKM
|
Characteristics |
Test method / (classification) |
Units |
Expression of resulta |
|